Influence of Copaifera multijuga hayne oil-based emulsion on the stability of the dentin matrix
Influência da emulsão à base de óleo de Copaifera multijuga hayne na estabilidade da matriz dentinária
Palavras-chave:
Dentina, Fitoterapia, Colágeno, ClorexidinaResumo
The objective of this work was to analyze the elastic response of dentin to the biomodification of the organic matrix with the use of an emulsion based on Copaíba oil. Sound human third molars, 0.5 mm x 1.7 mm x 7 mm, were prepared, 90 samples were obtained, demineralized, radiographed and tested at baseline and immersed for 30 and 60 minutes in the test substances: GC1 (distilled water); GEC (Copaiba oil-based emulsion); GCLX (2% Chlorhexidine). The modulus of elasticity (ME) was evaluated immediately after biomodification and at 3, 7 and 14 days after treatment. The specimens were tested in 3-point flexion with a 5 N load cell. The data were submitted to statistical analysis using parametric test of mixed three-way ANOVA. All groups showed a decrease in ME over time. The immersed specimens from the GEC group showed the highest values after 3 and 7 days. It was concluded that the treatment of collagen with all the test substances at 30 and 60 min of immersion immediately reduced the ME, however the GEC group was the one that presented the highest values of the mean modulus of elasticity, promoting greater stability throughout the period. evaluation time.
Downloads
Referências
ANGKER, L. et al. Micro-mechanical characterisation of the properties of primary tooth dentine. J Dent, v. 31, n. 4, p. 261-267, 2003. DOI: 10.1016/s0300-5712(03)00045-9
ARAÚJO, E. M. et al. Effect of a Copaiba Oil-Based Dental Biomodifier on the Inhibition of Metalloproteinase in Adhesive Restoration. Advances in Pharmacological and PharmaceuticalSciences, v. 2021, p. 1-10, 2021. DOI: 10.1155/2021/8840570
BANDEIRA, M. F. C. L. et al. Adhesive resistance of a copaiba oil-based dentin biomodifier. Braz. oral res., v. 34,p. 1-10, 2020. DOI: 10.1590/1807-3107bor-2020.vol34.0001
BANDEIRA, M.F.C. L. et al. Dentin Cleaning Ability of an Amazon Bioactive: Evaluation by Scanning Electron Microscopy. The Open Dent J, v. 10, n.1, p. 182- 87, 2016. DOI: 10.2174/1874210601610010182
BEDRAN-RUSSO, A. K. B. et al. Mechanical properties of tannic-acid-treated dentin matrix. Journal of dental research, v. 88, n. 9, p. 807-811, 2009. DOI: 10.1177/0022034509342556
BEDRAN-RUSSO, A. K. et al. Long-term effect of carbodimide on dentin matrix and resindentin bonds. J Biomed Mater Res B Appl Biomater, v. 94, n.1, p. 250-255, 2010. DOI: 10.1002/jbm.b.31649
BEDRAN-RUSSO, A.K.B. et al. Changes in stiffness of demineralized dentin following application of collagen crosslinkers. Journal of biomedical materials research. Part B, Applied biomaterials, v. 86, n. 2, p. 330-334, 2008. DOI: 10.1002/jbm.b.31022
BEDRAN-RUSSO, Ana K. et al. Dentin biomodification: strategies, renewable resources and clinical applications. Dental materials, v. 30, n. 1, p. 62-76, 2014. DOI: 10.1016/j.dental.2013.10.012
BETANCOURT, D.E et al. . Resin-Dentin bonding interface: Mechanisms of degradation and strategies for stabilization of the hybrid layer. Int J Biomater, v. 2019, p.1-11, 2019. DOI: 10.1155/2019/5268342
BRESCHI, L. et al. Chlorhexidine stabilizes the adhesive interface: a 2 year in vitro study. Dental Materials, v. 26, n. 4, p. 320-325, 2010. DOI: 10.1016/j.dental.2009.11.153
BRESCHI, L. et al. Dental adhesion review: aging and stability of the bonded interface. Dental materials, v. 24, n. 1, p. 90-101, 2008. DOI: 10.1016/j.dental.2007.02.009
BRESCHI, L. et al. Dentin bonding systems: From dentin collagen structure to bond preservation and clinical applications. Dental Materials, v. 34, n.1. p. 78-96, 2018. DOI: 10.1016/j.dental.2017.11.005
BRESCHI, L.et al. Influence of chlorhexidine concentration on the durability of etch-andrinse dentin bonds: a 12-month in vitro study. J. Adhes. Dent, v. 11, n. 3, p. 191-198, 2009. https://pubmed.ncbi.nlm.nih.gov/19603582/
BRIDI, E. C. et al. Long-term evaluation of the stability of dentin matrix following treatments with aqueous solutions of titanium tetrafluoride at different concentrations. Archives of oral biology, v. 91, p. 51-56, 2018. DOI: 10.1016/j.archoralbio.2018.04.006
CARRILHO, M.R.O. et al. Chlorhexidine Preserves Dentin Bond in vitro. J. Dent. Res, v.81, n.1, p. 90-94, 2007. DOI: 10.1177/154405910708600115
CASTELLAN, C. S. et al. Long-term stability of dentin matrix following treatment with various natural collagen cross-linkers. J Mech Behav Biomed Mater. vol. 4, n. 7, p. 1343-1350, 2011. DOI: 10.1016/j.jmbbm.2011.05.003
CASTELLAN, C. S. et al. Mechanical characterization of proanthocyanidin-dentin matrix interaction. Dental Materials, v. 26, n.10, p. 968–973, 2010. DOI: 10.1016/j.dental.2010.06.001
DE BARI, C.C. et al.; Amazon emulsions as cavity cleansers: antibacterial activity, cytotoxicity and changes in human tooth color. Rev. bras.farmacogn, v.26; n.4; p.497-501, 2016. DOI: https://doi.org/10.1016/j.bjp.2016.03.010
DELGADO, C. C. et al. Redução da atividade proteolítica da dentina após curtos períodos de aplicação de proantocianidina. Rev. odontol. UNESP, v. 44, n. 6, p. 355-359, 2015. DOI: https://doi.org/10.1590/1807-2577.02115
DOS SANTOS, P. H; KAROl S.; BEDRAN-RUSSO A. K; Nanomechanical properties of biochemically modified dentin bonded interfaces. J Oral Rehabil, v. 38, n.7, p. 541-546, 2011. DOI: 10.1111/j.1365-2842.2010.02175.x
EPASINGHE, D. J. et al. Effect of flavonoids on the mechanical properties of demineralised dentine. Journal of dentistry, v. 42, n. 9, p. 1178-1184, 2014. DOI: 10.1016/j.jdent.2014.07.002
FARES, N.H. et al. Resistência flexural e módulo de elasticidade da resina composta. Rev de Clin Pesq Odontol, v.2, p. 53-5, 2005.
FERREIRA, Andreza Camurça et al. Biomodifying Effect of Different Cross-Linking Agents on the Mechanical Properties of Dentin Collagen. Rev. Bras. Odontol, v. 77, p. 1836-1841, 2020. DOI: http://dx.doi.org/10.18363/rbo.v77.2020.e1836
FRASSETTO, A. et al. Mechanisms of degradation of the hybrid layer in adhesive dentistry and therapeutic agents to improve bond durability—A literature review. Dental Materials, v. 32, n. 2, p. 41-53, 2016. DOI: 10.1016/j.dental.2015.11.007
HEBLING, J. et al. Chlorhexidine arrests subclinical degradation of dentin hybrid layers in vivo. J Dent Res, v. 84, n. 8, p. 741-6, 2005. DOI: 10.1177/154405910508400811
KARAS, et al. Galloylation of polyphenols alters their biological activity. Food and Chemical Toxicology, v. 105, p. 223-240, 2017. DOI: 10.1016/j.fct.2017.04.021
LAFUENTE, D. SEM Analysis of Hybrid Layer and Bonding Interface After Chlorhexidine Use. Oper Dent. v.37, n.2, 172-180, 2012. DOI: 10.2341/10-251-L
LIU, Yi et al. Enhancement in dentin collagen's biological stability after proanthocyanidins treatment in clinically relevant time periods. Dental Materials, v. 29, n. 4, p. 485-492, 2013. DOI: 10.1016/j.dental.2013.01.013
MEIRA, D. F. J et al. Avaliação histomorfométrica do efeito de um biomodificador de dentina à base de óleo de copaiba (Copaifera multijuga Hayne) na camada híbrida. Brazilian Journal of Development, v. 6, n. 9, p. 65445-65458, 2020. DOI:10.34117/bjdv6n9-104
MOREIRA, M. A. et al. Effectiveness of new natural biomodification agents of Anacardiaceae extracts in dentin collagen cross-linking. Dental materials, v.33,n.10, p. 1103-1109, 2017. DOI: 10.1016/j.dental.2017.07.003
MOURA, L. G. et al. . Dentin surface and hybrid layer morphological analysis after use of a copaiba oil- based dentin biomodifier. Conjecturas, [S. l.], v. 21, n. 4, p. 78–97, 2021. DOI: 10.53660/CONJ-155-30
NIU, Li-na et al. Biomimetic remineralization of dentin. Dental materials, v. 30, n. 1, p. 77- 96, 2014. DOI: 10.1016/j.dental.2013.07.013
PASHLEY, D. H. et al. State of the art etch-and-rinse adhesives. Dental materials, v. 27, n. 1, p. 1-16, 2011. DOI: 10.1016/j.dental.2010.10.016
RIOS, L. F. F.. et al. Chlorhexidine does not improve but preserves bond strength to eroded dentin. American journal of dentistry, v. 28, n. 1, p. 28-32, 2015. https://pubmed.ncbi.nlm.nih.gov/25864239/
SABBAGH, J.; VREVEN, J.; LELOUP, G.; Dynamic and static moduli of elasticity of resinbased materials. Dental Materials, v. 18, n. 1. p. 64-71, 2002. DOI: 10.1016/s0109-5641(01)00021-5
VIDAL, C.M.P. et al. Galloyl moieties enhance the dentin biomodification potential of plantderived catechins. Acta biomaterialia, v. 10, n. 7, p. 3288-3294, 2014. DOI: 10.1016/j.actbio.2014.03.036
XU, H. H.et al. Indentation damage and mechanical properties of human enamel and dentin. J Dent Res, v. 77, p. 472-480, 1998. DOI: 10.1177/00220345980770030601